BUSBARS
RECTANGULAR SHAPED BARE COPPER BUSBARS
Size | a (mm) | b (mm) | X-Section (mm2)* | Unit Weight (kg/m) |
25×3 | 3 | 25 | 74 | 0,66 |
30×3 | 3 | 30 | 89 | 0,80 |
25×4 | 4 | 25 | 99 | 0,88 |
30×4 | 4 | 30 | 119 | 1,06 |
20×5 | 5 | 20 | 99 | 0,88 |
25×5 | 5 | 25 | 124 | 1,10 |
30×5 | 5 | 30 | 149 | 1,33 |
30×10 | 10 | 30 | 299 | 2,65 |
32×10 | 10 | 32 | 319 | 2,83 |
40×5 | 5 | 40 | 199 | 1,77 |
40×10 | 10 | 40 | 399 | 3,54 |
50×5 | 5 | 50 | 249 | 2,22 |
50×10 | 10 | 50 | 499 | 4,43 |
50×15 | 15 | 50 | 749 | 6,65 |
60×5 | 5 | 60 | 299 | 2,66 |
60×10 | 10 | 60 | 599 | 5,32 |
60×12 | 12 | 60 | 719 | 6,39 |
60×15 | 15 | 60 | 899 | 7,98 |
75×6 | 6 | 75 | 449 | 3,99 |
80×5 | 5 | 80 | 399 | 3,55 |
80×10 | 10 | 80 | 799 | 7,10 |
80×15 | 15 | 80 | 1199 | 10,65 |
80×20 | 20 | 80 | 1599 | 14,20 |
90×10 | 10 | 90 | 899 | 7,99 |
92×5 | 5 | 92 | 459 | 4,08 |
100×5 | 5 | 100 | 499 | 4,44 |
100×8 | 8 | 100 | 799 | 7,10 |
100×10 | 10 | 100 | 999 | 8,88 |
100×12 | 12 | 100 | 1199 | 10,66 |
100×15 | 15 | 100 | 1499 | 13,32 |
100×20 | 20 | 100 | 1999 | 17,76 |
100×30 | 30 | 100 | 2999 | 26,64 |
110×6 | 6 | 110 | 659 | 5,86 |
120×5 | 5 | 120 | 599 | 5,33 |
120×10 | 10 | 120 | 1199 | 10,66 |
120×12 | 12 | 120 | 1439 | 12,79 |
120×15 | 15 | 120 | 1799 | 15,99 |
120×20 | 20 | 120 | 2399 | 21,32 |
125×10 | 10 | 125 | 1249 | 11,11 |
128×5 | 5 | 128 | 639 | 5,69 |
130×7 | 7 | 130 | 909 | 8,09 |
140×10 | 10 | 140 | 1399 | 12,44 |
170×10 | 1699 | 15.13 |
ROUNDED SHAPE COPPER BARS
Delivered in diameters of Ø 5-70 mm and in lengths 1 – 6 m. |
SQUARE AND HEXAGONAL COPPER BARS
Delivered in diameters of Ø 8-60 mm and in lengths 1 – 6 m. |
BUSBAR PACKING
Packing Type | Dimensions | Net Weight (kg) | Tare (kg) | |||
---|---|---|---|---|---|---|
A | B | C | E | |||
Wooden box | 350-500 | 200-500 | 100 | 2.500-6.300 | 500-1.000 | 40-180 |
COPPER: MECCHANICCAL CHARACTERISTICS
Designation | Size mm |
Hardness
|
Tensile
strengthRm |
Yield point
0,2 % Rp 0,2 |
Elongation
|
|||||||||||||||
Round,
square hexagonal |
Flat
|
A100 mm
|
A
|
|||||||||||||||||
Material |
Thickness
|
Widht
|
HB
|
HV
|
N/mm2
|
N/mm2
|
%
|
%
|
||||||||||||
Symbol | Number |
Hardness
|
from
|
over
of |
up to and including
|
from
|
over
of |
up to and including
|
from
|
over
of |
up to and including |
min.
|
max.
|
min.
|
max.
|
min.
|
min.
|
min.
|
||
D
|
2
|
–
|
80
|
0,5
|
–
|
40
|
1
|
–
|
200
|
Drawn product
without any mecchaniccal characteristics. |
||||||||||
H035*
|
2
|
–
|
80
|
0,5
|
–
|
40
|
1
|
–
|
200
|
35
|
65
|
35
|
65
|
–
|
–
|
–
|
–
|
|||
Cu-ETP | CW004A |
R200*
|
2
|
–
|
80
|
1
|
–
|
40
|
5
|
–
|
200
|
–
|
–
|
–
|
–
|
200
|
max.120
|
25
|
35
|
|
Cu-OF | CW008A |
H065
|
2
|
–
|
80
|
0,5
|
–
|
40
|
1
|
–
|
200
|
65
|
90
|
70
|
95
|
–
|
–
|
–
|
–
|
|
NOTE : 1 N/mm2 is equivalent in 1 MPa. – * Annealing |